Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 7 potx

... 37 150 22 21 56 67 145 21 110 16 485 70 290 42 Sheet, hard rolled 290 42 220 32 15 73 83 160 23 180 26 495 72 325 47 Extruded bar, rod, and solid shapes 255 37 200 29 12 49 57 130 19 97 ... Sheet, annealed 230 33 125 18 17 48 55 115 17 76 11 350 51 200 29 Sheet, hard rolled 240 35 180 26 7 54 65 115 17 125 18 395 57 270 39 Extruded bar and shapes 255 37 180 26 12 44 45 125 18 83 ... sheet(b) 21 70 235 34 170 25 130 19 8 200 400 125 18 115 17 105 15 30 260 500 110 16 105 15 105 15 25 315 600 97 14 83 12 83 12 15 370 70 0 76 11 55 8 55 8 50 HM21A-T5 forgings(c) 21 70 230...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 14 doc

... 0.18 × 10 -7 59.0 7. 00 0.28 × 10 -7 63.6 8 .75 0.44 × 10 -7 68.2 10.50 0.88 × 10 -7 74 .9 12.25 1.18 × 10 -7 78 .7 14.00 2.00 × 10 -7 83 .7 15 .75 2. 57 × 10 -7 86.2 Source: Ref 579 Electrical ... 97. 79 -153 101.58 -113 106.1 -73 108.9 -23 110.8 27 113. 17 1 27 116 .7 2 27 120.2 3 27 123.9 4 27 1 27. 8 5 27 132.0 900 190 β phase 940 179 1040 179 γ phase 1050 160 1300 160 The ... 571 . J.A. Lee, P.G. Mardon, J.H. Pearce, and R.O.A. Hall, J. Phys. Chem. Solids, Vol 11, 1959, p 177 -181 572 . H.A. Eick and R.N.R. Mulford, J. Chem. Phys., Vol 41, 1964, p 1 475 -1 478 573 ....

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 2 docx

... 500 76 11 62 9 55 316 600 52 7. 5 41 6 75 371 70 0 34 5 28 4 100 -196 -320 634 92 586 85 5 -80 -112 558 81 531 77 5 -28 -18 538 78 510 74 5 24 75 5 17 75 490 71 5 100 212 483 70 462 67 6 ... 371 70 0 34 5 28 4 100 -196 -320 579 84 469 68 11 -80 -112 496 72 4 07 59 10 -28 -18 483 70 400 58 10 24 75 476 69 393 57 10 100 212 448 65 372 54 10 149 300 310 45 248 36 17 204 400 179 ... . . . 525 76 490 71 8 76 11.0 . . . . . . . . . . . . . . . -28 -18 . . . 505 73 470 68 8 74 10 .7 . . . . . . . . . . . . . . . 24 75 . . . 485 70 450 65 8 72 10.5 485 70 450 65 8...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 3 pdf

... 6.0 T51 179 26 124 18 3.0 T6 278 40 2 07 30 6.0 A356.0 T71 2 07 30 138 20 3.0 E 172 25 90 13 5.0 T51 179 26 1 17 17 3.0 T6 345 50 296 43 2.0 3 57. 0 T7 278 40 234 34 3.0 A3 57. 0 T6 3 17 46 248 ... B535.0 4 5 4 4 1 1 4 70 5.0 5 4 4 4 2 1 4 70 7.0 5 4 4 4 2 1 4 71 0.0 5 3 4 4 2 1 4 71 1.0 5 4 5 4 3 1 3 71 2.0 4 4 3 3 3 1 4 71 3.0 4 4 3 4 2 1 3 77 1.0 4 4 3 3 2 1 . . . 77 2.0 4 4 3 3 2 1 . . ... 70 5.0 F/T5 (205) (30, min) (1 17) ( 17, min) (5, min) F/T5 (2 27) (33, min) (152) (22, min) (2, min) 70 7.0 F/T7 (255) ( 37, min) (2 07) (30, min) (1, min) 241 35 172 ...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 4 pot

... C71500 (copper-nickel, 30%) 70 .0 Cu, 30.0 Ni F, R, T 372 -5 17 54 -75 138-483 20- 70 45-15 20 C7 170 0 67. 8 Cu, 0 .7 Fe, 31.0 Ni, 0.5 Be F, R, W 483-1 379 70 -200 2 07- 1241 30-180 ... 20 C72500 88.2 Cu, 9.5 Ni, 2.3 Sn F, R, W, T 379 -8 27 55-120 152- 74 5 22-108 35-1 20 C73500 72 .0 Cu, 10.0 Zn, 18.0 Ni F, R, W, T 345- 75 8 50-110 103- 579 15-84 37- 1 20 C74500 ... 1 .75 Pb, 37. 5 Zn, 0 .75 Sn F, R, S 379 -531 55 -77 172 -365 25-53 40-15 70 C50500 (phosphor bronze, 1.25% E) 98 .75 Cu, 1.25 Sn, trace P F, W 276 -545 40 -79 97- 345 14-50 48-4...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 5 docx

... min 170 min 25 min 25 min . . . O50 520-590 75 -85 395-530 57- 77 11- 17 81-89 H02 565-620 82-90 505-605 73 -88 3-13 85-88 H08 605- 670 88- 97 585-650 85-94 2-5 87- 90 Hardness. ... 50 270 39 25 55 HRB 54 240 35 H02 395 57 340 49 12 65 HRB 60 255 37 H04 485 70 395 57 5 77 HRB 68 290 42 H06 540 78 420 61 4 83 HRB 72 305 44 H08 580 84 435 63 3 86 HRB 74 315 ... 11 58 HRB 56 240 35 H04 420 61 370 54 5 70 HRB 63 260 38 H06 460 67 400 58 4 75 HRB 67 275 40 H08 495 72 425 62 3 78 HRB 69 290 42 M20 270 39 97 14 44 60 . . . 215 31 Flat products,...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 6 ppt

... 3-13 2 -7 SiO2 D 52.5 . . . . . . 7. 5 . . . . . . 5 SiO2; 15 Bi W 72 4 .7 3.3 3.5 8 .7 1.4 1.9 SiO2; 0.2 Al2O3 W, D 72 7 3 6 6 . . . 3 SiO2; 4 MoO3 D 62 7 8 12 7 . . . 4 sand D ... in./rev) Annealing temperature. 650 to 74 5 °C (1200 to 1 375 °F) CNZ-1818- 17 1 17 17 234 34.0 140 20.0 11.0 75 11.0 500 73 32.5 24.0 7. 90 172 25.0 90 CNZP-1816- (b) (b) (b) ... 26 .7 24.1 37. 8 6.04 6.15 (890) . . . 99.64 . . . . . . . . . 0.24 0.03 2 .78 24 . . . 0.6 8 .7 34.1 56.6 5.95 7. 85 (1140)(a) . . . 99.62 . . . . . . . . . 0.26 0.03 2 .71 27 . . . 0.3 5.7...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 8 pdf

... 4928, 4930, 4965-49 67, 4 970 , 4 971 , 4 973 , 4 974 , 4 976 , 4 978 , 4 979 , 4981, 4983, 4984, 4986, 49 87 4921, 4924, 4926, 4928, 4930, 4965, 49 67, 4 970 -4 972 , 4 974 , 4 975 , 4 977 -4981, 4995, 4996 ... standards (TIS)(b) TIS 79 12 TIS 76 07 TIS 79 15 Rod, TIS 79 15; Wire, TIS 79 16 TIS 79 13, TIS 79 14 . . . . . . South Korean standards D 5 577 . . . D5604 Rod, D 5604; Wire, D 5 576 ; ... for Testing and Materials (ASTM) B 265 B 381 and F 620 Bar and billet, B 348, F 67 . . . B 3 37 and B 338 . . . Nuts, F 4 67; Bolts, F 468; Surgical implants, F 67, F 136 and F 620 ...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 9 pptx

... 652 1205 652 -76 0 1205-1400 BAg-8 P 077 20 71 .0 -73 .0 bal . . . . . . . . . . . . . . . . . . 0.15 77 9 1435 77 9 1435 77 9-889 1435-1650 BAg-8a P 077 23 71 .0 -73 .0 bal . . . ... hardened condition, 171 115 5 17 319 558 414 77 74 Static (24.8) (16 .7) (75 ) (46.5) (81) (60) (11.2) (10.8) 169 121 5 27 378 . . . 476 . . . . . . Dynamic (24.5) ( 17. 6) (76 .5) (54.8) (69) Poisson's ... . 0.15 671 1240 77 9 1435 77 9-899 1435-1650 BAg-5 P 074 53 44.0-46.0 29.0-31.0 23.0- 27. 0 . . . . . . . . . . . . . . . 0.15 663 1225 74 3 1 370 74 3-843 1 370 -1550...

Handbook Properties and Selection Nonferrous Alloys and Spl Purpose Mtls (1992) WW Part 11 docx

... of Fe-Ni alloys between 0 and 38 °C Ni, % Mean coefficient, μm/m · K 31.4 3.395 + 0.00885 t 34.6 1. 373 + 0.002 37 t 35.6 0. 877 + 0.001 27 t 37. 3 3.4 57 - 0.006 47 t 39.4 5.3 57 - 0.00448 ... annealed 260 38 470 68 37 75 10% cold worked 370 54 565 82 23 86 30% cold worked 550 80 675 98 10 95 50% cold worked 640 93 72 5 105 5 96 70 % cold worked 70 3 102 73 0 106 3 97 K14052 (glass-sealing ... 0.12 0. 07 38 .70 340 645 2.50 0.24 0.03 41.88 375 71 0 4.85 . . . . . . 42.31 380 71 5 5. 07 . . . . . . 43.01 410 77 0 5 .71 . . . . . . 45.16 425 800 7. 25 0.35 ...

Xem thêm

Từ khóa: Báo cáo thực tập tại nhà thuốc tại Thành phố Hồ Chí Minh năm 2018 chuyên đề điện xoay chiều theo dạng Nghiên cứu tổ chức pha chế, đánh giá chất lượng thuốc tiêm truyền trong điều kiện dã ngoại Nghiên cứu tổ hợp chất chỉ điểm sinh học vWF, VCAM 1, MCP 1, d dimer trong chẩn đoán và tiên lượng nhồi máu não cấp Giáo án Sinh học 11 bài 13: Thực hành phát hiện diệp lục và carôtenôit Giáo án Sinh học 11 bài 13: Thực hành phát hiện diệp lục và carôtenôit ĐỒ ÁN NGHIÊN CỨU CÔNG NGHỆ KẾT NỐI VÔ TUYẾN CỰ LY XA, CÔNG SUẤT THẤP LPWAN ĐỒ ÁN NGHIÊN CỨU CÔNG NGHỆ KẾT NỐI VÔ TUYẾN CỰ LY XA, CÔNG SUẤT THẤP LPWAN NGHIÊN CỨU CÔNG NGHỆ KẾT NỐI VÔ TUYẾN CỰ LY XA, CÔNG SUẤT THẤP LPWAN SLIDE Quản lý hoạt động học tập của học sinh theo hướng phát triển kỹ năng học tập hợp tác tại các trường phổ thông dân tộc bán trú huyện ba chẽ, tỉnh quảng ninh Phối hợp giữa phòng văn hóa và thông tin với phòng giáo dục và đào tạo trong việc tuyên truyền, giáo dục, vận động xây dựng nông thôn mới huyện thanh thủy, tỉnh phú thọ Phát hiện xâm nhập dựa trên thuật toán k means Nghiên cứu, xây dựng phần mềm smartscan và ứng dụng trong bảo vệ mạng máy tính chuyên dùng Nghiên cứu về mô hình thống kê học sâu và ứng dụng trong nhận dạng chữ viết tay hạn chế Nghiên cứu tổng hợp các oxit hỗn hợp kích thƣớc nanomet ce 0 75 zr0 25o2 , ce 0 5 zr0 5o2 và khảo sát hoạt tính quang xúc tác của chúng Định tội danh từ thực tiễn huyện Cần Giuộc, tỉnh Long An (Luận văn thạc sĩ)Tăng trưởng tín dụng hộ sản xuất nông nghiệp tại Ngân hàng Nông nghiệp và Phát triển nông thôn Việt Nam chi nhánh tỉnh Bắc Giang (Luận văn thạc sĩ)Giáo án Sinh học 11 bài 14: Thực hành phát hiện hô hấp ở thực vật BÀI HOÀN CHỈNH TỔNG QUAN VỀ MẠNG XÃ HỘI QUẢN LÝ VÀ TÁI CHẾ NHỰA Ở HOA KỲ