High Temperature Strain of Metals and Alloys Part 1 ppt

High Temperature Strain of Metals and Alloys Part 1 ppt

High Temperature Strain of Metals and Alloys Part 1 ppt

... Republic of GermanyPrinted on acid-free paperISBN -13 : 978-3-527- 313 38-9ISBN -10 : 3-527- 313 38-9Valim Levitin High Temperature Strain of Metals and Alloys High Temperature Strain of Metals and Alloys, ... Deformation of Some Refractory Metals 14 38 .1 The Creep Behavior 14 38.2 Alloys of Refractory Metals 14 98.3 Summary 15 5Supplements 15 7Supplement 1: On Dislocations in the Crystal Lattice 15 7Supplement ... 3-527- 313 389-9VContentsIntroduction 1 1 Macroscopic Characteristics of Strain of Metallic Materialsat High Temperatures 52 In situ X-ray Investigation Technique 13 2 .1 Experimental Installation 13 2.2 Measurement Procedure 15 2.3...
  • 15
  • 303
  • 0
High Temperature Strain of Metals and Alloys Part 2 pptx

High Temperature Strain of Metals and Alloys Part 2 pptx

... restEI698 0.08 14 .0 1. 65 2.70 – 2.99 – 0.003 2.04 restEI867 0.02 9.5 4.47 – 5.26 9.82 5 .12 0.020 – restEP199 0.05 19 .8 2 .14 1. 42 9 .10 4.54 – 0.008 – rest High Temperature Strain of Metals and Alloys, ... beendetermined by the X-ray method at high temperatures.Pure metals, solid solutions and nickel-based superalloys have been stud-ied. High Temperature Strain of Metals and Alloys, Valim Levitin (Author)Copyrightc ... screw 10 to the stem of the valve. The elongation of the specimen is measured witha clock indicator 14 with an accuracy of 0. 01 mm.The chamber 18 and covers 17 have special windows 19 made of...
  • 15
  • 269
  • 0
High Temperature Strain of Metals and Alloys Part 3 pdf

High Temperature Strain of Metals and Alloys Part 3 pdf

... 4.42.6 12 .8 2.2 4.3V 0.55 12 06 3.7 17 .2 1. 6 4.54.2 19 .6 1. 4 4.6 1. 3 5.9 1. 8 4 .1 0.60 13 18 1. 7 7.8 1. 5 5.62 .1 9.8 1. 2 5 .1 0.7 6.0 1. 5 3.80. 51 923 1. 3 11 .0 1. 6 4.4Fe 1. 7 14 .0 0.8 4.50.4 3.0 1. 5 ... 3.3 12 .0 44 .1 1.2 3.34.6 17 .2 1. 5 2.4Nb 0.55 15 08 7.2 27.0 1. 3 2.57.6 28.4 1. 1 3.42 .1 7.8 1. 6 2.20.60 16 45 2.6 9.8 1. 3 2.73 .1 11. 8 1. 1 3.25.3 24.5 1. 9 3.60.50 10 96 6.3 29.4 1. 5 4 .1 7.4 ... 697± 12 24Nb 15 08 17 .2 13 0 ± 10 12 0 ± 10 12 028.4 92 ± 795± 11 37 16 45 9.8 12 0 ± 10 93 ± 9 68 11 .8 97 ± 895± 9 18 5V 10 96 24.5 80 ± 890± 8 11 534.3 67 ± 660± 7 35673 11 0.0 55 ± 356± 5 85 14 0.0...
  • 15
  • 321
  • 0
High Temperature Strain of Metals and Alloys Part 4 ppsx

High Temperature Strain of Metals and Alloys Part 4 ppsx

... ˙ε, 10 −7s 1 V, nm s 1 ˙ε, 10 −7s 1 Ni+9.9Al 723 12 5 52 1. 4 4.3 2.2202 34 10 .1 7.6 11 .5873 70 54 0.9 2.8 1. 0 13 6 33 13 .9 8.2 13 .0Ni+9.5W 873 13 8 41 5.6 12 .0 7.8 17 0 33 17 .6 8.6 26.0 10 23 ... in the literature, e.g. [ 21, 22]. For example, Ev=2.56 × 10 19 Jat. 1 , Uv =1. 92 × 10 19 Jat. 1 for α-iron, and 2.88 × 10 19 Jat. 1 and 1. 68 × 10 19 Jat. 1 , respectively, for nickel. ... lines) and computed data (solidcurves) 1, 10 23K;2, 11 73K.4.6 Formation of Jogs 55Fig. 4 .10 Comparison of the temperature dependence of the creep rates ˙ε under stress of 80 MPa (a) and of themean-square...
  • 15
  • 254
  • 0
High Temperature Strain of Metals and Alloys Part 5 pdf

High Temperature Strain of Metals and Alloys Part 5 pdf

... 12 0◦60◦a2 [11 0]√22 [11 0] 0◦a2[¯ 11 0]√22[ 011 ] 60◦b.c.c. {11 0} 90◦a2 [11 1]√22 [11 0] 35.3◦a2 [1 ¯ 11 ]√22 [1 ¯ 10 ] 35.3◦73.2◦a2 [11 1]√22[¯ 1 ¯ 10 ] 14 4.7◦a2 [1 ¯ 11 ]√66 [1 ¯ 21] ... 90◦a2 [11 0]√22 [11 0] 0◦a2[¯ 11 0]√22[¯ 11 0] 0◦60◦a2 [11 0]√22 [11 0] 0◦a2 [10 ¯ 1] √22 [10 ¯ 1] 0◦60◦a2[ 011 ]√22[¯ 1 ¯ 10 ] 12 0◦a2[¯ 11 0]√22[0¯ 11 ] 12 0◦60◦a2 [11 0]√22 [11 0] ... DensityWe have obtained Eq. (4 .19 ). Hencedρ 1 dt= δρ 1 V 1 + δsρs1V 1 − 0.5D2 1 V 1 ρ2.5 1 − ρ 1 V 1 D 1 (5.3)4.8 Stability of Dislocation Sub-boundaries 59Fig. 4 .14 A sub-boundary formed...
  • 15
  • 409
  • 0
High Temperature Strain of Metals and Alloys Part 6 doc

High Temperature Strain of Metals and Alloys Part 6 doc

... are of the same order, 10 11 m−2. For examplethemeasured density is (1. 3–9.5) × 10 11 m−2in nickel, (1. 6–5.3) × 10 11 m−2in niobium and so on.From Figs. 5.9 and 5 .10 it can be seen that ... differently.The density of mobile dislocations increases during the high- temperature strain from 2 10 8m−2to (4.0–4.5) 10 11 m−2. Experimental data have thesame order of 10 11 m−2. The total ... preliminary decreased value of λ and increased value of D lead to the strain rate decreasing when the applied stress is relatively low. High Temperature Strain of Metals and Alloys, Valim Levitin (Author)Copyrightc...
  • 15
  • 265
  • 0
High Temperature Strain of Metals and Alloys Part 7 pot

High Temperature Strain of Metals and Alloys Part 7 pot

... 6.σ2/σ 1 , ∆U, 10 19 Jat. 1 Ref.T , K MPa/MPa N2/N 1 10 10 10 11 10 12 923 600/400 30.3 3.56 3.87 4 .18 author 10 23 280/80 11 5 .1 3.68 4. 01 4.33 35973 360/280 6.0 3.97 4.28 4.59 37 10 23 320/200 ... range 10 10 10 12 m−2, most likely 10 12 m−2.Applying Eq. (6 .14 ) for tests of the same superalloy under two stresses σ 1 and σ2 and denoting the sums of the first three terms as A 1 and ... 94 6 High- temperature Deformation of SuperalloysFig. 6 .15 Electron micrographs of the EP199 superalloy.T = 11 73K; σ = 11 0MPa. (a), (b) At the end of thesteady-state stage of creep; ×65000....
  • 15
  • 281
  • 0
High Temperature Strain of Metals and Alloys Part 8 docx

High Temperature Strain of Metals and Alloys Part 8 docx

... [ 011 ] 0. 41 [10 1] 0. 4111 0] 0 (1 ¯ 11 ) [ 011 ] 0. 4110 1] 0. 41 [11 0] 0[¯ 11 1] (11 1) [¯ 11 0] 0.27 a/2[¯ 11 0] → a/6[¯ 12 1] + a/6[¯ 21 ¯ 1] +APB[¯ 10 1] 0.27[0¯ 11 ] 0 [11 1] (¯ 11 1) [11 0] ... [¯ 10 1] 0. 41 a/2[¯ 10 1] → a/6[¯ 11 2] + a/6[¯2¯ 11 ]+APB[0¯ 11 ] 0. 41 [11 0] 0(¯ 11 1) [0¯ 11 ] 0. 41 a/2[0¯ 11 ] → a/3 [1 ¯ 12 ] + a/6[¯2¯ 1 ¯ 1] +SISF [10 ¯ 1] 0. 4111 0] 0(¯ 1 ¯ 11 ) [ 011 ] ... ∆θ[0 01] ∆θ[ 011 ]∆θ [11 1]Rupture life, h 1 42.6 8.8 26.5 58.02 23.6 20.4 38 .1 64.03 24.4 19 .8 38.0 88.34 39.9 20.0 18 .3 10 3.05 39.5 20.6 18 .6 10 6.06 14 .5 30.9 42.4 11 8.07 42.0 23.8 14 .8 14 3.38...
  • 15
  • 340
  • 0
High Temperature Strain of Metals and Alloys Part 9 potx

High Temperature Strain of Metals and Alloys Part 9 potx

... mode of lattice deformation of CMSX-4 superalloy changes from {11 1} < 11 2 > at 10 23K to {11 1} < 11 0 >at 12 23K. The authors suggest that the occurrence of {11 1} < 11 2 > and {11 1} ... proposed:a/2 (11 1)[ 01 ¯ 1] + a/2 (1 ¯ 11 )[ 011 ] → a[ 010 ] (7.3)ora/2 (11 1)[ 01 ¯ 1] + a/2 (1 ¯ 11 )[0¯ 1 ¯ 1] → a[00¯ 1] (7.4)The separation distance between the individual a/2 < 11 0 > dislocationsis ... the (11 1)plane, combine to produce the leading half of the a< ;11 2 > ribbon:a/2 [10 ¯ 1] + a/2[ 01 ¯ 1] → a/2 [11 ¯2]“The second step” consists in the dissociation:a/2 [11 ¯2] → a/3 [11 ¯2]...
  • 15
  • 239
  • 0
High Temperature Strain of Metals and Alloys Part 11 docx

High Temperature Strain of Metals and Alloys Part 11 docx

... 2.0 – –EI867 9.5 4.5 – 9.8 5.3 5 .1 – – – –EP199 19 .8 2 .1 1.4 4.5 9 .1 – – – – –ZhS6UVI 9.4 5.6 2.5 1. 5 10 .1 9.6 – 1. 1 – 0.5HfZhS26VI 5.0 5.8 0.9 1. 1 11 .5 8.9 – 1. 4 – 0.9VRene N5 7.0 6.2 – 2.0 ... plane of type {11 1} in the < 11 0 > direction. TheBurgers vector is e.g.b = a/2 [11 0]. The dissociation happens according tothe reactiona2 [11 0] =a6 [12 1] +a6[ 21 ¯ 1] (S .1) Two ... creepstrength of alloys: P = T [15 + log t 1% ]10 3(8 .1) where T is temperature of the tests, t 1% is the time of 1% deformation of aspecimen, 15 is an empirically determined value. 15 2 8 Deformation of...
  • 15
  • 287
  • 0

Xem thêm

Từ khóa: magnetic properties of metals and alloysself propagating high temperature synthesis of ultrafine tungsten carbide powdersintegrated approach for hazard assessment of metals and inorganic metal substances the unit world model approachbioaccumulation hazard identification of metals and inorganic metal substancesaquatic toxicity for hazard identification of metals and inorganic metal substancesstructure properties and processing relationships in metals and alloysthe methylation of metals and metalloids in aquatic systemsvero cells infected with the edmonston strain of mv and stained with a fluorescently labeled antibody to mv1introduction specificity of high temperature use of porous materials in foundry applicationshigh temperature electrolysis of steamhazard identification of metals and inorganic metal substancesastm e 527 83 2003 numbering metals and alloys unskaplan toefl paper and pencil part 1the turn of the screw 1999 part 1history of internet and world wide web pptNghiên cứu sự biến đổi một số cytokin ở bệnh nhân xơ cứng bì hệ thốngNghiên cứu tổ hợp chất chỉ điểm sinh học vWF, VCAM 1, MCP 1, d dimer trong chẩn đoán và tiên lượng nhồi máu não cấpđề thi thử THPTQG 2019 toán THPT chuyên thái bình lần 2 có lời giảiGiáo án Sinh học 11 bài 13: Thực hành phát hiện diệp lục và carôtenôitGiáo án Sinh học 11 bài 13: Thực hành phát hiện diệp lục và carôtenôitĐỒ ÁN NGHIÊN CỨU CÔNG NGHỆ KẾT NỐI VÔ TUYẾN CỰ LY XA, CÔNG SUẤT THẤP LPWANPhát triển mạng lưới kinh doanh nước sạch tại công ty TNHH một thành viên kinh doanh nước sạch quảng ninhNghiên cứu, xây dựng phần mềm smartscan và ứng dụng trong bảo vệ mạng máy tính chuyên dùngSở hữu ruộng đất và kinh tế nông nghiệp châu ôn (lạng sơn) nửa đầu thế kỷ XIXTổ chức và hoạt động của Phòng Tư pháp từ thực tiễn tỉnh Phú Thọ (Luận văn thạc sĩ)Kiểm sát việc giải quyết tố giác, tin báo về tội phạm và kiến nghị khởi tố theo pháp luật tố tụng hình sự Việt Nam từ thực tiễn tỉnh Bình Định (Luận văn thạc sĩ)Quản lý nợ xấu tại Agribank chi nhánh huyện Phù Yên, tỉnh Sơn La (Luận văn thạc sĩ)BT Tieng anh 6 UNIT 2Giáo án Sinh học 11 bài 15: Tiêu hóa ở động vậtGiáo án Sinh học 11 bài 14: Thực hành phát hiện hô hấp ở thực vậtGiáo án Sinh học 11 bài 14: Thực hành phát hiện hô hấp ở thực vậtGiáo án Sinh học 11 bài 14: Thực hành phát hiện hô hấp ở thực vậtTrách nhiệm của người sử dụng lao động đối với lao động nữ theo pháp luật lao động Việt Nam từ thực tiễn các khu công nghiệp tại thành phố Hồ Chí Minh (Luận văn thạc sĩ)BÀI HOÀN CHỈNH TỔNG QUAN VỀ MẠNG XÃ HỘIHIỆU QUẢ CỦA MÔ HÌNH XỬ LÝ BÙN HOẠT TÍNH BẰNG KIỀM